Clay Graphite Crucible

  • Clay Graphite Crucible
  • Clay Graphite Crucible
  • Clay Graphite Crucible
  • Clay Graphite Crucible
Model No.︰1
Brand Name︰HBXYYGE
Country of Origin︰China
Unit Price︰US $ 100 / pc
Minimum Order︰5 pc
Share on:

 Total 14 Related Items 
Prev1011121314Next

Product Description

Graphite crucible is a utensil or melting tank vessels which use graphite powder and clay as main raw material, made through pressing in different molds (according to different needs) and firing process.

Clay graphite crucible advantages:
High strength (Flexural strength: 30Mpa Compressive strength: 55Mpa with rising of temperature, graphite strength increases)
High temperature resistance (graphite material melting point is 3850±50C)
Good heat shock resistance
Anti-oxidation,
Strong corrosion resistance to acid and alkali liquid
Abrasion resistance,
Good conductivity and thermal efficiency.
Excellent chemical stability
Small thermal expansion coefficient.
Easy to clean

 

Clay graphite crucible application:
Graphite crucible, with its special advantages and Plasticity, is widely used in the smelting area, e.g. gold smelting, silver smelting, aluminum smelting, and cooper smelting in metallurgy, casting, machinery, chemical and other industries.

Clay graphite crucible Operating Notice:
The crucible should be stocked in the dry situation.
Carry the crucible carefully
Warm the crucible in the drying machine or near the furnace. The warming temperature should be up to 500℃.
The crucible should be put under the furnace mouth flat.
When put the metal into the crucible, you should take the crucible capacity as your reference. If the crucible is too full, it will be damaged by expansion.
The clamps shape need as that of crucible. Avoid the concentrate stressed destroy of the crucible.
Clean the crucible regularly and gently.
The crucible should be put in the center of the furnace and leave some distance between the crucible and furnace.
Turn the crucible once a week and this will help prolong the service life.
The flame should not touch the crucible directly.

 

 

Clay graphite crucible Technical Index 

Standard parameter

Test result

refractoriness

1630℃

refractoriness

1635℃

Carbon content

38%

Carbon content

41.46%

apparent porosity

35%

apparent porosity

32%

bulk density

1.6g/cm3

bulk density

1.71g/cm3

 

Clay graphite crucible Physical properties

Specifications

Unit

Value

Bulk Density

g/cm3

1.65-1.80

Compressive Strength *

MPa

20-55

Bending Strength *

MPa

10-30

Elastic Modulus *

GPa

9-21

Specific Resistance *

u.Ω.m

5.0-15.0

Ash

%

0.05-0.5

Payment Terms︰TT
Product Image





Related Products
Stopper Rod
Stopper Rod
US $ 80
Aluminum-magnesium spinel ramming material
Aluminum-magnesium spinel ramming material
US $ 580
refractory castable
refractory castable
US $ 1
Vanadium-Nitrogen alloy
Vanadium-Nitrogen alloy
US $ 180




Home  |  Product Catalog  |  News  |  Contact Us  |  Sitemap  |  Mobile Version

Powered by DIYTrade.com  Build your FREE website !